Description :
DENEPOX™ 40 is an ultra low viscosity, 2 components epoxy injection resin for structural injections in concrete in both dry and wet environments.
Technical Information :
| Property | Value | Norm |
| Bonding strength on dry concrete | Exceeds coherence of concrete | ISO 4624 |
| Bonding strength on damp concrete | Exceeds coherence of concrete | ISO 4624 |
| Compressive strength | Approx. 100N/mm² | NBN EM 196 |
| Tensile strength | > 50 N/mm² | |
| Bending strength | > 60 N/mm | NBN EM 196 |
| Elongation at break | < 10% | |
| Glass transition temperature | < 60°C | EN 12614 |
| Density | 1-1.1kg/dm³ | |
| Viscosity (mixture) at 25°C | Approx. 85 | Test DNC |
| Pot life | Approx. 80 minutes (100 g at 25°C) | Test DNC |
| Minimum application temperature | Approx. 10°C |
Full chemical or mechanical resistances are only reached after a curing period of 7 days at 20°C. Mechanical properties of epoxy resins decrease at temperatures higher than 50°C.
Packing : 3kg pail comprising - Part A : 2.3kg, Part B : 0.7kg in metal pails.
简介 :
DENEPOX™40是一种超低粘度的双组分环氧树脂注射灌浆，用在干燥和潮湿环境中的混凝土结构注射。
技术资料：
| 项目 | 值 | 测试标准 |
| 干混凝土粘结强度 | 超过混凝土的附著性 | ISO 4624 |
| 湿混凝土粘结强度 | 超过混凝土的附著性 | ISO 4624 |
| 抗压强度 | ~100N/mm² | NBN EM 196 |
| 抗拉强度 | > 50 N/mm² | |
| 抗弯强度 | > 60 N/mm | NBN EM 196 |
| 断裂伸长率 | < 10% | |
| 玻璃化转变温度 | < 60°C | EN 12614 |
| 密度 | 1-1.1kg/dm³ | |
| 粘度(混合物) @ 25°C | ~ 85 | DNC测试 |
| 使用时限 | ~ 80 分钟 (100 克@ 25°C) | DNC测试 |
| 最低使用温度 | ~ 10°C |
在20℃下7天的固化时间后，才能达到完整的抗化学或抗机械性能。环氧树脂的机械性能在高于50℃的温度下会降低。
包装：3公斤配套，包含A组分：2.3公斤， B组分：0.7公斤。
Penerangan :
DENEPOX ™ 40 adalah jenis grout suntikan epoksi 2 komponen dengan kelikatan ultra rendah untuk suntikan struktur konkrit dalam keadaan kering dan basah.
Informasi Teknikal :
| Ciri-ciri | Nilai | Kaedah Ujian |
| Kekuatan lekatan pada konkrit kering | Melebihi kepaduan konkrit | ISO 4624 |
| Kekuatan lekatan pada konkrit basah | Melebihi kepaduan konkrit | ISO 4624 |
| Kekuatan mampatan | ~ 100N/mm² | NBN EM 196 |
| Kekuatan tegangan | > 50 N/mm² | |
| Kekuatan lenturan | > 60 N/mm | NBN EM 196 |
| Pemanjangan takat putus | < 10% | |
| Suhu peralihan kaca | < 60°C | EN 12614 |
| Ketumpatan | 1-1.1kg/dm³ | |
| Kelikatan (campuran) @ 25°C | ~ 85 | Ujian DNC |
| Masa penggunaan | ~ 80 min (100 g @ 25°C) | Ujian DNC |
| Suhu penggunaan minimum | ~ 10°C |
Ketahanan bahan kimia atau mekanikal yang lengkap hanya dicapai selepas tempoh pengesetan 7 hari pada 20°C. Sifat-sifat mekanikal resin epoksi menurun apabila suhu melebihi 50°C.
Pembungkusan : 3kg baldi terdiri daripdada Bahagian A: 2.3kg, Bahagian B: 0.7kg dalam baldi logam.