SUJ2 Suppliers - AISI 52100 Bearing Steel, EN31, 100Cr6, 1.3505
The common name for this type of Bearing Steel is SUJ2 , the JIS Standard Alloy Bearing Steel, Origin Japan Bearing Steel.
Bearing steel 52100 is one kind of special steel with features of high wear resistance and rolling fatigue strength.
AISI 52100 / SUJ2 Alloy Steel is known as a high carbon , chromium containing low alloy steel.
* Please refer to this blog for our export to Indonesia : https://www.ecarbonsteel.com/index.php?ws=latestnews&nid=92423
Advantages of Chrome Bearing Steel 52100:
-
Superior hardness, 60-67 on Rockwell hardness scale (Rc) at room temperature
-
High carbon chrome alloy steel
-
Operates continually at temperatures up to 120°C
-
Used to produce precision ball bearings and roller bearings
-
Cost-effective
-
Long working life
ASTM 52100 Bearing Steel is equivalent to
|
Country |
USA |
German |
Japan |
British |
|
Standard |
ASTM A295 |
DIN 17230 |
JIS G4805 |
BS 970 |
|
Grades |
52100 |
100Cr6/1.3505 |
SUJ2 |
535A99/EN31 |
Chemical Composition of JIS SUJ2
|
Element |
Content (%) |
|
Iron, Fe |
96.5 – 97.32 |
|
Chromium, Cr |
1.30 – 1.60 |
|
Carbon, C |
0.980 – 1.10 |
|
Manganese, Mn |
0.250 – 0.450 |
|
Silicon, Si |
0.150 – 0.300 |
|
Sulfur, S |
≤ 0.0250 |
|
Phosphorous, P |
≤ 0.0250 |
Mechanical Properties of 1.3505 Alloy Steel
|
Properties |
Metric |
Imperial |
|
Bulk modulus (typical for steel) |
140 GPa |
20300 ksi |
|
Shear modulus (typical for steel) |
80 GPa |
11600 ksi |
|
Elastic modulus |
190-210 GPa |
27557-30458 ksi |
|
Poisson’s ratio |
0.27-0.30 |
0.27-0.30 |
|
Hardness, Brinell |
– |
– |
|
Hardness, Knoop (converted from Rockwell C hardness) |
875 |
875 |
|
Hardness, Rockwell C (quenched in oil from 150°C tempered) |
62 |
62 |
Forging of AISI 52100 Steel
EN31 alloy steel is forged at 927 to 1205°C, and should not be forged below 925ºC. A post-forge equalization treatment is recommended at 745ºC for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.
Heat Treatment of AISI 52100 , SUJ2 Steel
SUJ 2 alloy steel is heated at 816°C (1500°F) followed by quenching in oil. Before performing this process, it is subjected to normalizing heat treatment at 872°C (1600°F) followed by slowly cooling in order to reduce the machining stress.
Hardening of SUJ2 Steel
100Cr6 alloy steel is hardened by cold working, or heating and quenching. It can be carburized at 913°C (1675°F) followed by quenching. It is again heated at 788°C (1450°F) followed by quenching for the second time.
Applications for SUJ2 , 52100 Steel
Alloy Steel 52100 Grade Bearing Steel is mainly used for the manufacture of aircraft bearings and other highly stressed parts. This steel grade SUJ2 Steel is preferably vacuum arc re-melted to give optimum performance.
Typical applications: Bearing Manufacture, CV joints, ball screws, gauges, knife etc.
Our Sales & Supplier Network
Australia, Pakistan, Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.
E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors. We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.
Lebih maklumat tentang E STEEL SDN. BHD.
Malaysia