Stainless Steel SS416 is a free machining basic straight chromium high hardenability martensitic stainless steel with excellent machinability, reasonable strength and corrosion resistance.
We supply and export to Singapore , Indonesia , Brunei and other ASEAN Countries.
Our specialty is to provide wide range of stainless steel with no minimum order (MOQ).
E Steel supply Stainless Steel SUS416 (SS416) Round Bars / Rods / Shaft , SUS416 (SS416) Plates.
E Steel is glad to export and supply SUS416 Stainless Steel to Singapore , may refer : https://www.ecarbonsteel.com/index.php?ws=latestnews&nid=96232
| Grade 416 Stainless Steel | Min. % | Max. % | |
| *Nickel & Molybdenum addition optional. | Carbon | 0.09 | 0.15 |
| Silicon | 0 | 1.00 | |
| Manganese | 0 | 1.50 | |
| *Nickel | 0 | 1.00 | |
| Chromium | 11.50 | 14.00 | |
| *Molybdenum | 0 | 0.60 | |
| Phosphorous | 0 | 0.06 | |
| Sulphur | 0.15 | 0.35 | |
| Tempering Temperature (°C) | Tensile Strength (MPa) |
Yield Strength 0.2% Proof (MPa) |
Elongation (% in 50mm) |
Hardness Brinell (HB) |
Impact Charpy V (J) |
| Annealed * | 517 | 275 | 30 | 262 | – |
| Condition T ** | 758 | 586 | 18 | 248-302 | – |
| 204 | 1340 | 1050 | 11 | 388 | 20 |
| 316 | 1350 | 1060 | 12 | 388 | 22 |
| 427 | 1405 | 1110 | 11 | 401 | # |
| 538 | 1000 | 795 | 13 | 321 | # |
| 593 | 840 | 705 | 19 | 248 | 27 |
| 650 | 796 | 670 | 17.5 | 253 | 38 |
* Tempering of this steel at temperatures of 400 to 580°C should be avoided due to low impact resistance.
| Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
| BS | En | No | Name | ||||
| ss416 | S41600 | 416S21 | 56AM | 1.4005 | X12CrS13 | 2380 |
SUS 416 |
While sus416 displays a reasonable resistance to scaling in continuous service up to 650 oC, it does however experience a substantial drop in tensile strength, creep and stress rupture strength at relatively low working temperatures. It is also susceptible to hot cracking due to its high sulphur content.
NB. High temperature use is therefore not generally recommended.
416SS is not recommended for use at sub-zero temperatures due to a substantial drop in impact properties consistent with most steels other than the austenitic steel types.
S41600 due to its higher sulphur content has lower resistance to all corrosion types than grade SUS410, and indeed all of the 400 series martensitic stainless steels.
Its selection therefore is generally based upon its excellent machinability coupled with its lower corrosion resistance capabilities.
NB. It has optimum corrosion resistance in the hardened and tempered condition and is not therefore recommended for use in the annealed condition.
It is most important that oxygen is always allowed to circulate freely on all stainless steel surfaces to ensure that a chrome oxide film is always present to protect it. If this is not the case, rusting will occur as with other types of non stainless steels.
For optimum corrosion resistance surfaces must be free of scale and foreign particles.
Finished parts should be passivated.