ALUMINIUM PLATE/BAR/ROD/PIPE/ANGEL/SECTION

Specifications:

• 6061-T6
• 5052
• 5083
• 7075
• 1100

Typical Chemical Composition (6061-T6):

• Cu: 0.15-0.40%
• Mn: 0.0-0.15%
• Fe: 0.0-0.7%
• Mg: 0.80-1.20%
• Si: 0.40-0.80%
• Zn: 0.0-0.25%
• Ti: 0.0-0.15%
• Cr: 0.04-0.35%
• Al: Remaining %

Typical Mechanical Properties (6061-T6):

• Tensile Strength: 310 MPa
• Elongation: 12%
• Proof Stress: 270 MPa
• Shear Strength: 190 MPa
• Hardness Vickers: 100 HV

Applications (6061-T6):

• Rail coaches
• Truck frames
• Ship building
• Bridges and military bridges
• Aerospace applications including helicopter rotor skins
• Tube
• Pylons and towers
• Transport
• Boilermaking
• Motorboats
• Rivets

Typical Chemical Composition (5052):

• Al: 95.7-97.7%
• Cr: 0.15-0.35%
• Cu: 0.1% max
• Fe: 0.4% max
• Mg: 2.2-2.8%
• Mn: 0.1% max
• Si: 0.25% max
• Zn: 0.1% max

Typical Mechanical Properties (5052):

• Tensile Strength: 193 MPa
• Yield Strength: 89.6 MPa
• Hardness: 47 HB
• Elongation: 25%
• Modulus of Elasticity: 70.3 GPa
• Machinability: 30%

Applications (5052):

• Architecture
• General sheet metal work
• Heat exchangers

Typical Chemical Composition (5083):

• Cr: 0.05-0.25%
• Cu: 0.40-1.00%
• Fe: 0.40% max
• Mg: 4.00-4.90%
• Mn: 0.10% max
• Si: 0.40% max
• Zn: 0.25% max
• Ti: 0.15% max
• Al: Remaining %

Typical Mechanical Properties (5083):

• Tensile Strength: 330 MPa
• Hardness: 95 HB
• Elongation: 17%
• Modulus of Elasticity: 72 MPa
• Proof Strength: 240 MPa
• Shear Strength: 185 MPa

Applications (5083):

• Known for exceptional performance in extreme environments
• Used in rail cars
• Vehicle bodies
• Tip truck bodies
• Mine skips and cages
• Pressure vessels

• Used in shipbuilding due to its high resistance to attack by seawater and chemical environments
• Alloy 5083 also retains exceptional strength after welding, having the highest strength of the non-heat treatable alloys but is not recommended for use in temperatures in excess of 65degC

Typical Chemical Composition (7075):

• Al: 87.1-91.4%
• Cr: 0.18-0.28%
• Cu: 1.2-2%
• Fe: 0.5% max
• Mg: 2.1-2.9%
• Mn: 0.3% max
• Si: 0.4% max
• Ti: 0.2% max
• Zn: 5.1-6.1%

Typical Mechanical Properties (7075):

• Tensile Strength: 572 MPa
• Yield Strength: 503 MPa
• Hardness: 150 HB
• Elongation: 11%
• Modulus of Elasticity: 71.7 GPa
• Machinability: 70%

Applications (7075):

• Used in transport applications, including marine, automotive and aviation, due to their high strength-to-density ratio
• Rock climbing equipment
• Bicycle components
• Inlineskating-frames
• Hang glider airframes

Typical Chemical Composition (1100):

• Al: 99.0%
• Cu: 0.12%

Typical Mechanical Properties (1100):

• Modulus of Elasticity: 70-80 GPa

Applications (1100):

• Widely used in fin stock
• Heat exchanger fins
• Spun hollowware
• Dials and name plates
• Decorative parts
• Giftware
• Cooking utensils
• Rivets
• Reflectors
• Sheet metal work

General Aluminium Applications:

• Greyish-white in colour, it is malleable, ductile and conductive to heat and electricity
• This film of oxide can be further thickened by a process known as the anodizing
• Welding can be made possible
• Anodized or spray coating possible to achieve different architectural effects
• I-beams and special aluminium profiles are also available
• A thin inert film of oxide products the metal surface from further attack, thus giving the metal a form of resistance to corrosion
• With its non-corrosive and good mechanical properties, each grade of Aluminium has a high range of applications
• Aluminium also possesses very high malleability, enabling it to be produced into a very thin foil.

Profiles Available:

• Round Bar / Rod
• Flat Bar
• Square Bar
• Angle Bar
• Hollow Section
• Pipe / Tube
• Wire
• Shim / Foil
• Sheet / Plate
• Perforated (Sheet)
• “T”, “L”, “U”, “I” Bar
• Conveyor System (Racking)