CuNi2Be / CW 110C / UNS C17510 / W. Nr. 2.0850
Technical Data Sheet
Alloy 3 is an alloy strengthened with copper, nickel, and beryllium. This material is widely used in various industries due to its high-temperature resistance, excellent mechanical properties, and high wear resistance.
Specification
|
Forms |
ASTM & ASME & SAE |
|
Bar |
ASTM B441, ASTM B534, EN 12167, SAE J461, SAE J463 |
|
Rod |
ASTM B441, EN 12163, EN 12164, SAE J461, SAE J463 |
|
Tube |
ASTM B937, ASTM B944, SAE J461, SAE J463 |
|
Plate |
ASTM B534, SAE J461, SAE J463 |
|
Sheet |
ASTM B534, SAE J461, SAE J463 |
|
Forging |
ASTM B870, ASTM B938, EN 12165, SAE J461, SAE J463 |
Application
Used for Automotive, Chemical processing, Marine, Metal & plastic moulding and Thermal industry, etc.
Examples:
Connectors, Conductors, Die Casting Plunger Tips, Fasteners, Fuse Clips, High Flux Electromagnets, Instrument Parts, Thermal Transfer Plates, Welding Equipment, etc.
Chemical Composition Limits Wt.% (According to ASTM B441)
|
Element |
Be |
Co |
Ni |
Fe |
Al |
Si |
Cu |
|
Min. |
0.2 |
|
1.4 |
|
|
|
Balance |
|
Max. |
0.6 |
0.3 |
2.2 |
0.10 |
0.2 |
0.2 |
Balance |
Typical Mechanical Properties
|
Material |
Condition |
Hardness HRB |
Tensile Strength |
0.2% Yield Strength |
Elongation in 4D |
Modulus of Elasticity |
|
MPa |
MPa |
% |
kN/mm2 |
|||
|
Alloy 3 |
HT (TH04) |
95-102 |
750-970 |
650-870 |
5-25 |
138 |
Typical Physical Properties
|
Material |
Temperature |
Density |
Density before age hardening |
Specific heat capacity |
Thermal conductivity |
Electrical conductivity |
Melting range |
|
g/cm3 |
g/cm3 |
J/kg K |
W/m K |
MS/m |
℃ |
||
|
Alloy 3 |
HT (TH04) |
8.83 |
8.75 |
420 |
240 |
32 |
1000-1070 |
Standard product forms
Bar (Round & flat), Extrusions, Forging, Plate, Profiles, Rod, Sheet, Strip, Tube, etc.
Services
Every order is treated as carefully and timely as possible, and shipments are handled to ensure that all export procedures are followed correctly so that your order arrives in perfect condition as quickly as possible.
Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.