AISI 8620, 1.6523, SNCM220 Case Hardening Steel

AISI 8620, 1.6523, SNCM220 Case Hardening Steel

分类: Alloy Steel 当前有货
欲了解更多详情,请游览我们的官方网站 ecarbonsteel.com

详情

AISI 8620 Suppliers - Alloy Steel 1.6523, SNCM220 Case Hardening Steel 

AISI 8620 is a low-nickel-chromium-molybdenum medium hardenability, case hadening (carburizing) steel, which generally supplied in the as rolled condition with a maximum brinell hardness of 280 (RC30).  

ASTM 8620 Steel is characterised by good core strength and toughness in small to medium sections with case hardness up to Rc62 when carburized, hardened and tempered.

AISI 8620 Case Hardening Steel can also be used (uncarburised) as a high tensile steel, which when suitably hardened and tempered can be utilized for various applications requiring good tensile strength and reasonable  toughness.

Pre hardened and tempered (uncarburized) Material 8620 can be further surface hardened by nitriding but will not respond satisfactorily to flame or induction hardening due to its low carbon content.

SAE 8620 steel (carburized) is used extensively by all industry sectors for light to medium stressed components and shafts requiring high surface wear resistance with reasonable core strength and impact properties.


Chemical Composition of AISI 8620 

C Mn P S Si Mo Ni Cr
0.18-0.23 0.7-0.9 max 0.035 max 0.040 0.15-0.35 0.15-0.25 0.4-0.7 0.4-0.7


Applications of Material Material 8620  | 1.6523 Case Harden Steel

Caburized splined shafts, piston pins, cam shafts, guide pins, bushings, automotive differential pinions and transmissions, arbors, bearings, sleeves king pins, carburized gears, general engineering purposes.

SAE 8620 Steel is equivalent to 

Country USA DIN BS BS Japan
Standard ASTM A29 DIN 1654 EN 10084 BS 970 JIS G4103
Grades 8620 1.6523/
21NiCrMo2
1.6523/
20NiCrMo2-2
805M20 SNCM220

 

Mechanical Properties of Case Hardening Steel 8620 

Properties Metric Imperial
Tensile strength 530 MPa 76900 psi
Yield strength 385 MPa 55800 psi
Elastic modulus 190-210 GPa 27557-30458 ksi
Bulk modulus (typical for steel) 140 GPa 20300 ksi
Shear modulus (typical for steel) 80 GPa 11600 ksi
Poisson’s ratio 0.27-0.30 0.27-0.30
Izod Impact 115 J 84.8 ft.lb
Hardness, Brinell 149 149
Hardness, Knoop (converted from Brinell hardness) 169 169
Hardness, Rockwell B (converted from Brinell hardness) 80 80
Hardness, Vickers (converted from Brinell hardness) 155 155
Machinability (hot rolled and cold drawn, based on 100 machinability for AISI 1212 steel) 65 65



Heat Treatment of ASTM 8620 



Machinability of SAE 8620 Material 


The 8620 alloy steel is readily machined after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment – after carburizing machining is usually limited to grinding.



Welding of Alloy Steel 8620 Materials


The 8620 Alloy Steel may be welded as rolled condition by conventional methods, usually gas or arc welding.

Preheating at 400F is beneficial and subsequent heating after welding is recommended – consult the approved weld procedure for the method used. However, welding in the case hardened or through hardened condition is not recommended




Our Sales & Supplier Network

Australia, Pakistan,  Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.

E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors.  We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.  


更多 E STEEL SDN. BHD. 相关资料
E STEEL SDN. BHD.
E STEEL SDN. BHD. Stainless Steel Supplier Malaysia, Titanium Supply Selangor, Nickel Alloy Supplies Kuala Lumpur (KL) ~ E STEEL SDN. BHD.