UDIMET L-605 / UNS R30605
Technical Data Sheet
Alloy L-605 is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000! (1093℃) with good resistance to sulfidation, wear and galling. The high temperature strength results from solid-solution strengthening by tungsten with second phase strengthening by precipitated carbides.
Specification
|
Forms |
SAE |
|
Bar |
SAE AMS 5759 |
|
Plate |
SAE AMS 5537 |
|
Forgings |
SAE AMS 5759 |
Application
Used for Gas turbine, Industrial furnace, etc.
Examples: Blades, Combustion chamber parts, Liners, Mufflers, Rings, etc.
Chemical Composition Limits Wt.% (According to SAE AMS 5759)
|
Element |
C |
Mn |
Si |
P |
S |
Cr |
Ni |
W |
Fe |
Co |
|
Min |
0.05 |
1.00 |
|
|
|
19.00 |
9.00 |
14.00 |
|
Remainder |
|
Max |
0.15 |
2.00 |
0.40 |
0.040 |
0.030 |
21.00 |
11.00 |
16.00 |
3.00 |
Remainder |
Typical Mechanical Properties
|
Material |
Temperature |
Yield Strength 0.2% |
Tensile Strength |
Elongation |
Hardness HB |
||
|
ksi |
Mpa |
ksi |
Mpa |
||||
|
Alloy L-605 Bar |
RT |
45 |
310 |
125 |
862 |
30 |
277 max |
Standard product forms
Bars, Foil, Forgings, Forging Stock, Plate, Sheet, Strip, Rings, Wire, etc.
Services
Every order is treated as carefully and timely as possible, and shipments are handled to ensure that all export procedures are followed correctly so that your order arrives in perfect condition as quickly as possible.
Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.