Akasel Cold Mounting resins cure through a chemical reaction and provides protection/support of the sample surface by MSP Metrology (M) Sdn Bhd from Akasel Denmark.
Cold mounting resins typically consist of two components that cure after being mixed together. Two different systems are available, epoxies and acrylics. The epoxies consist of a liquid resin and a liquid hardener.
Our epoxy resin can be mixed with either the Aka-Cure Slow or Aka-Cure Quick hardener, depending on the requirements. They all have very good adhesion to the sample, which helps to provide the best possible edge retention. They can also be used for vacuum impregnation of fragile and porous samples like ceramics and plasma spray coatings.
We offer epoxy resin and hardeners separate, not as a kit, to make it easy to use either hardener with the resin. Epoxies require good precision when mixing the two components. It can be measured by volume, but weighing is much more precise and the recommended method. Our acrylic resin consists of a powder and a liquid.
Aka-Clear-2 is a fast curing, transparent system with a slightly yellowish tint. It cures in 8 minutes and produces totally clear, bubble-free mounts without having to use a pressure pot.
Mixing of the 2 components is not critical, if a thinner mix is required, a little extra liquid can be added without adverse effect on the cured mounts. With Aka-Clear Powder we ship 2 measuring spoons, 2 reusable mixing cups and 25 wooden mixing pins for easy measuring and mixing of the resin. With the Aka-Resin Epoxy we ship the same, except the measuring spoons, as the epoxy resin and hardener should be measured by weight and not by volume.
| Type | Epoxy | Acrylic | |
| Component 1 |
Aka-Resin Liquid Epoxy Viscosity: 600-700 cps @25°C |
Aka-Clear-2 Powder | |
| Component 2 |
Aka-Cure, Slow Viscosity: 20 cps @25°C |
Aka-Cure, Quick Viscosity: 80 cps @25°C |
Aka-Clear-2 Liquid |
| Mixing ratio by weight |
100 g of resin : 12 g of Aka-Cure, Slow |
100 g of resin : 26.3 g of Aka-Cure, Quick |
10 g of powder : 6.3 g of liquid |
| Mixing ratio by volume |
100 parts of resin : 13.5 parts of Aka-Cure, Slow |
100 parts of resin : 30 parts of Aka-Cure, Quick |
2 parts of powder : 1 part of liquid |
| Curing time | 8-24 hours @ 22°C. Long pot life and low peak temperature, suitable for both vacuum impregnation and mounting of heat sensitive samples. Not suitable for large mounts due to exces sive exothermal reaction. |
30 min. when heated to 80°C. Peak temperature up to 200°C. For very hard, transparent mounts. Very large mounts can be made using a 2 cycle curing schedule. First, the mount is cured without heating in 8 hours, followed by a 1h cycle@ 100°C |
8-10 minutes @ 22°C. Peak temperature up to 90°C. |
|
Shrinkage, 1-5, 1 = best/lowest |
1 | 2 | 3 |
|
Recommended applications |
Transparent, very low curing temperature, no shrinkage, for sensitive materials.Vacuum impregnation. | Transparet, very fast epoxy system, for vauum impregnation of porous sample. | Completely clear for easy visibility of sample, mounting of electronic components, failure analysis. |
| Clear, low viscosity epoxy resin | |||
| Product no. | Product name | Contents | GRWT kg |
| 25101115 | Aka-Resin Liquid Epoxy | 1 L | 1.22 |
| 25101117 | Aka-Resin Liquid Epoxy | 5 L | 5.71 |
| Epoxy hardener, 8-24 hours cure @ 22°C | |||
| Product no. | Product name | Contents | GRWT kg |
| 25101213 | Aka-Cure Slow | 500 ml | 0.55 |
| Epoxy hardener, 30 min cure @ 80°C | |||
| Product no. | Product name | Contents | GRWT kg |
| 25101223 | Aka-Cure Quick | 500 ml | 0.55 |
| Clear acrylic resin, 8-10 min cure @ 22°C | |||
| Product no. | Product name | Contents | GRWT kg |
| 25202311 | Aka-Clear-2 Powder | 1 kg | 1.13 |
| 25202313 | Aka-Clear-2 Powder | 5 kg | 5.40 |
| 25202413 | Aka-Clear-2 Liquid | 500 ml | 0.81 |
| 25202415 | Aka-Clear-2 Liquid | 1 L | 0.99 |