RE Laminated Glass (Solar Control PVB Interlayer & Interlayer Discolor): Pilihan Utama di Singapore (SG) EASYTO (SINGAPORE) PTE. LTD.

Penerangan

Features:

High thermal insulation rate. The glass can adjust the indoor temperature by 7-15 degrees, saving more than 40% of energy for users in hot summer.
The EASYTO.1653R sunlight color change RE glass laminated film will automatically change color with the intensity of ultraviolet radiation, which enhance the thermal insulation performance, provides skin and temperature comfort and protect privacy. High-tech brings new visual effects.
The absorption spectrum is selected. RE laminated glass target and shield ultraviolet and infrared rays which is harmful to the human body, and allow the ambient light through that is beneficial to the human body. The ultraviolet blocking rate is 99.9%, the near-infrared blocking rate is 97.5%, and the near-infrared blocking rate of the sunlight color change type can even reach to more than 99.8%.
Noise reduction. Enhancing the sound insulation effect of glass.
Explosion-proof. The laminated film represents viscosity. Thus the glass will not fall off immediately once breaking, reducing the injury to people caused by the broken glass.
Stable performance, lifetime use.

Parameter

Physical Properties
Thickness(mm)	0.38mm	Width(mm)	0.65mm~3.2mm
Length	200m/roll	Color	Light Blue
Adhesive force percussion value	Level 9	Moisture Content	0.20%
Tensile Strength (MPa)	22.8 Kg/cm2	Tensile Elongation (%)	200
Static shrinkage	5%	Melt Index(g/10min)	18.5
UV resistance	UV wavelength313nm, 1000 hours, without Bubbles,cracks, slack
Resistance to damp and heat aging	100 °C, 100% RH,1000 hours, without Bubbles, cracks,slack
High temperature resistance	90 °C, 1000 hours,without Bubbles, cracks, slack

Physical Properties EASYTO. 1653
Blocked Infrared-light (%)	99.99%	Blocked UV-light (%)	97.5%
Haze	0.50%	Visible Light Transmittance (%)	70%
EASYTO. 1653R(Sunlight Color Change Type)
Blocked Infrared-light (%)	99.99%	Blocked UV-light (%)	99.8%
Haze	0.50%	Visible Light Transmittance (%)	15%~60%