The TI-5000 Series "exceeds the performance of traditional engineering plastics in almost all aspects."
Superior Balanced Physical Properties and Optimal for Heat-Resistant Gears
The TI-5000 Series boasts superior heat resistance (continuous use temperature of 250°C), heat distortion resistance (deflection temperature under load of 279°C), mechanical properties (especially tensile strength and shock resistance), fatigue resistance, flame retardance, friction and wear resistance, and stress crack resistance.
The TI-5000 Series “exceeds the performance of traditional engineering plastics in almost all aspects.”
The TI-200 Series is based on PPS resin, which offers superior heat resistance and flame retardancy, strengthened with special fibers. Its favorable moldability lends itself well for manufacturing with reliably high accuracy. The combination of high-strength grade TI-250A and sliding grade TI-200C not only gives this series low self-abrasion, but it also lowers the abrasion with other materials under extreme usage conditions of high temperature and high torque.
Property | Testing Method | Unit | 250A | 200C-H02 | 5013 | 5031 |
---|---|---|---|---|---|---|
Specific gravity | D792 | 1.67 | 1.67 | 1.40 | 1.45 | |
Water absorption (24 Hrs) | D570 | % | 0.02 | 0.02 | 0.33 | 0.28 |
Tensile strength | D638 | MPa | 200 | 165 | 186 | 157 |
Tensile elasticity | D638 | % | 2.3 | 1.9 | 15.0 | 8.0 |
Bending strength | D790 | MPa | 260 | 210 | 235 | 196 |
Bending elasticity | D790 | GPa | 12.7 | 10.5 | 4.9 | 6.4 |
Izod impact strength (notched) | D256 | J/m | 130 | 105 | 127 | 59 |
Deflection temperature under load (1.82 MPa) | D648 | °C | >260 | >260 | >278 | >279 |
Fiber reinforcing | Reinforced (PPS) |
Reinforced (PPS) |
Non-reinforced (PAI) |
Non-reinforced (PAI) |
||
High strength | High strength Wear resistance |
Ultrahigh strength Wear resistance |
Ultrahigh strength Wear resistance |
* This is a table of representative examples based on values measured from testing carried out under specific conditions.
The TI-200 Series is based on PPS resin, which offers superior heat resistance and flame retardancy, strengthened with special fibers. Its favorable moldability lends itself well for manufacturing with reliably high accuracy. In addition, the series has a superior application to the PTFE coating which makes the toner non-cohesive. The TI-7000 Series is based on PEEK, a resin whose heat resistance is better than that of TI-200, and reinforced by special fibers. Because of this, TI-7000 has a superior application to the PFA coating which improves toner non-cohesiveness much further.
Property | Testing Method | Unit | 240A | 7200 | 8000 | 7500 | 5013 | 550F |
---|---|---|---|---|---|---|---|---|
Specific gravity | D792 | 1.73 | 1.47 | 1.70 | 1.75 | 1.40 | 2.17 | |
Water absorption (24 Hrs) | D570 | % | 0.02 | 0.02 | 0.05 | 0.08 | 0.33 | 0.03 |
Tensile strength | D638 | MPa | 180 | 98 | 120 | 170 | 186 | 32 |
Tensile elasticity | D638 | % | 3.0 | 3.5 | 2.1 | 3.0 | 15.0 | 410 |
Bending strength | D790 | MPa | 270 | 127 | 190 | 280 | 235 | |
Bending elasticity | D790 | GPa | 18.0 | 6.9 | 12.9 | 14.0 | 4.9 | |
Izod impact strength (notched) | D256 | J/m | 45 | 25 | 30 | 127 | Nondestructive | |
Deflection temperature under load (1.82 MPa) | D648 | °C | >260 | >260 | >290 | >290 | 278 | |
Coating | PTFE | PTFE | PFA | PFA | PTFE | None | ||
Application example(s) | Fixing pawl | Fixing pawl | Fixing pawl | Fixing pawl | Fixing pawl Drum pawl |
Fixing pawl |
* This is a table of representative examples based on values measured from testing carried out under specific